Product Overview

This is a complete TIC composite wear parts set for the TRIO TP450 Cone Crusher, comprising one Bowl Liner (TRIO17023516) and one Mantle (TRIO17023515). Manufactured from high-manganese steel (Mn18Cr2) with embedded Titanium Carbide (TiC) ceramic composite inserts, these liners deliver 2–3 times the wear life of standard manganese steel parts. Direct-fit replacement — no modifications required.

TIC composite mantle (TRIO17023515) — green cone with visible TiC ceramic inserts (circular dots)

What is TIC Composite Wear Material?

TIC (Titanium Carbide) composite technology represents a major advancement in crusher wear part design. Hard TiC ceramic particles are embedded into a Mn18Cr2 high-manganese steel matrix during the casting process. The result is a wear surface that combines the extreme hardness of ceramics (HV 2400+) with the toughness and impact resistance of manganese steel.

Bowl Liner & Mantle: Working Principle

In a cone crusher, the Manteau (inner moving cone) and the Revêtement de cuvette (outer fixed concave) form the crushing chamber. As the mantle gyrates, rock is compressed and crushed between these two wear surfaces. Both parts are consumable — they wear progressively and must be replaced to maintain crushing efficiency and product gradation.

Bowl liner family — multiple sizes showing TIC composite construction

Key Features & Advantages

• Extended service life: TIC composite delivers 2–3× the wear life of standard Mn18Cr2, reducing downtime and replacement frequency
• Consistent product gradation: Wear-resistant TiC inserts maintain chamber profile longer, ensuring consistent output size throughout the liner lifecycle
• Reduced total cost of ownership: Fewer replacements = less labor, less downtime, lower per-ton crushing cost
• Direct OEM-equivalent fit: Precision-cast to TP450 specifications — drop-in replacement, no modifications needed
• Superior impact resistance: Mn18Cr2 steel matrix absorbs shock loads, preventing brittle fracture of ceramic inserts
• Work-hardening capability: The manganese steel matrix work-hardens under impact, becoming harder with use while TiC inserts provide continuous abrasion resistance
• Universal compatibility: Set includes both mantle and bowl liner for a complete chamber refresh

Typical Applications

Quarrying
Granite, basalt, limestone

Mining
Iron ore, copper, gold ore

Aggregates
Sand & gravel production

Construction
Road base, concrete aggregate

Recycling
Concrete & asphalt recycling

Demolition
Secondary/tertiary crushing

Material & Manufacturing Process

Base material: ASTM A128 Grade Mn18Cr2 — high-manganese austenitic steel with 18% Mn and 2% Cr, providing excellent work-hardening properties and impact toughness.

TIC inserts: Titanium Carbide (TiC) ceramic composite buttons are pre-placed in the mold at high-wear zones before pouring. During casting, the molten steel flows around and bonds with the TiC particles, creating a metallurgical bond between ceramic and steel.

Manufacturing route: Full-mold (lost-foam) casting or precision sand casting → controlled solidification → heat treatment (solution annealing + water quench) → rough and finish machining to OEM dimensions → final inspection.

Quality Control & Inspection

• Chemical composition analysis — Spectrometer verification of Mn, Cr, C, Si, P, S content per ASTM A128
• Mechanical hardness testing — Brinell HB measurement at multiple points (target: HB 220–260 for steel matrix)
• Dimensional inspection — CMM / template gauging against OEM drawings for profile accuracy
• Ultrasonic testing (UT) — Internal defect detection per ASTM E114
• TIC insert verification — Visual and dimensional check of ceramic insert distribution and bond quality
• Surface finish inspection — Visual + dye penetrant testing for surface cracks or defects
• Weight verification — Final weight recorded and compared to nominal (ref. 1312 kg/set)

Packaging & Shipping

Each liner is individually packaged in heat-treated (ISPM-15 compliant) wooden crates with steel banding and anti-corrosion VCI film wrapping. Crates are designed to withstand international container shipping. Suitable for both LCL and FCL container loading. Shipping marks and product labels applied per customer requirements.

Specification Table

The post TRIO17023516 & TRIO17023515 TIC Composite Bowl Liner + Mantle Set for TP450 Cone Crusher appeared first on Mining Spares | Crusher Spare Parts ,Drifter Parts ,Slurry Pump Parts.

Le manteau MP800 de MiningSpares utilise des alliages de manganèse de haute qualité, notamment les alliages 13% Standard, 18% Premium et 22% High, pour répondre aux diverses exigences opérationnelles et peut être personnalisé en fonction de vos besoins.
Nous proposons également différentes couleurs au choix : rouge, bleu, vert, noir, gris, etc.

Le processus de fabrication est très strict afin de garantir une adaptation parfaite à la machine.

Les manchons MP800 de MiningSpares sont fabriqués à l'aide de procédés de moulage avancés. Au cours du processus de fabrication, nous contrôlons strictement la sélection des matériaux et le déroulement du processus afin de garantir l'excellence de la qualité et des performances du produit. Nous utilisons des matériaux en acier allié de haute qualité combinés à une technologie de moulage avancée pour garantir que nos produits présentent une excellente résistance à l'usure et aux chocs. En outre, notre processus de fabrication comprend des procédés d'usinage de précision et de traitement thermique pour améliorer encore la résistance et la durabilité.

Pour la plupart des marques mondialement connues telles que Mettso, Sandvick, Terex, Shanbao, Telsmith, etc.
Nous disposons tous d'un stock important de dessins originaux, ce qui nous permet de produire à un coût relativement faible.

The post Mantle Liner 1050143952 Suit MP800 Shorthead Cone Crusher appeared first on Mining Spares | Crusher Spare Parts ,Drifter Parts ,Slurry Pump Parts.