High-manganese fixed and swing jaw plates manufactured by MiningSpares for the SAES CX120
European-type jaw crusher. SAES (Saes Makine Sanayi ve Ticaret A.Ş., Turkey) is an established
crushing and screening equipment manufacturer founded in 1992. The CX120 is their heavy-duty primary jaw crusher
designed for hard-rock quarrying and mining applications.

SAES CX120 Jaw Plate Specification Table

Material & Casting Process

All jaw plates are cast in Mn18% high-manganese steel (ASTM A128 Grade B2 equivalent)
using water-glass sand casting. Each plate undergoes solution heat treatment (water quenched) to achieve a fully
austenitic structure, then precision-machined on all mating surfaces for direct fitment into the SAES CX120 frame.
Key material properties:

• As-cast hardness: HB 200–220
• Work-hardened surface hardness in service: HB 450+
• Toughness: excellent impact resistance under high-compression crushing duty

Machine Data – SAES CX120 European Jaw Crusher

• Manufacturer: SAES (Saes Makine Sanayi ve Ticaret A.Ş., Turkey)
• Type: Heavy-duty primary jaw crusher (European type)
• Feed opening (width × depth): 1,200 × 870 mm
• Maximum feed lump size: 700 mm
• CSS (discharge setting) range: 70–200 mm (adjustable)
• Processing capacity: 175–610 t/h (material-dependent)
• Motor power: 160 kW (4-pole)
• Overall dimensions (L × W × H): 3,700 × 2,790 × 2,950 mm
• Drive: V-belt drive system with heavy flywheel inertia

Applications

SAES CX120 jaw plates are designed for primary crushing of medium-hard to hard rock in quarrying,
aggregate production, mining and construction-recycling operations — granite, basalt, limestone, diabase
and similar abrasive materials up to 700 mm feed size.

Frequently Asked Questions

Q1. What is the standard material grade?
Mn18% high-manganese steel (equivalent to ASTM A128 Gr.B2). Mn18Cr2 and Mn13Cr2 grades are available
on request for highly abrasive or high-impact duties.

Q2. Can I buy individual plates?
Yes. The fixed jaw (30721010) and swing jaw (30701020) can be ordered separately.

Q3. What is the lead time?
Machined plates from stock: 7–10 working days. Fresh castings: 25–35 days. Breakdown orders
can be expedited with air freight.

Q4. What documentation is supplied?
Every shipment includes spectrometer chemical-composition report, hardness test report and dimensional
inspection report. Third-party inspection (SGS, BV, TÜV) available on request.

Q5. Is this an OEM part?
No. These are aftermarket replacement parts manufactured by MiningSpares to original drawing specifications.
Not affiliated with or endorsed by SAES Makine.

Request a Quotation

For pricing, lead time and alternative material options on SAES CX120 jaw plates, use the
Ajouter à la demande button or email us at
[email protected]. Response within one business day.

The post 30721010 Fixed Jaw plate 30701020 Swing Jaw plate for SAES CX120 Crusher appeared first on Mining Spares | Crusher Spare Parts ,Drifter Parts ,Slurry Pump Parts.

High-manganese swing and fixed jaw plates manufactured by MiningSpares for the СМД-111
(SMD111) jaw crusher – the Russian-built primary jaw crusher also designated
ЩДП-9х12 and originally produced by Volgotsemmash (ОАО «Волгоцеммаш»).
The set consists of three cast manganese plates that form the primary crushing chamber: an upper and a lower
swing (movable) jaw plate running on the pitman, plus the stationary fixed jaw plate. Each plate is cast,
heat-treated and machined to drawing for direct replacement, with no frame modification required.

СМД-111 Jaw Plate Specification Table

Item 3 (3440.01.110) is a 2-piece (2P) fixed jaw plate design.

Material & Casting Process

All three plates are cast in Mn18% high-manganese steel (austenitic manganese steel,
equivalent to ASTM A128 Grade B2 / GOST 977-88 grade 110Г13Л) using water-glass sand casting. Each casting
is solution heat-treated (water quenched) to deliver a fully austenitic structure, then precision-machined on
all mating and seating faces so it seats correctly against the СМД-111 crusher frame and pitman.

• As-cast hardness: HB 200–220
• Work-hardened surface hardness in service: HB 450+
• Key benefit: the more the plate is impacted, the harder the working surface becomes –
  ideal for the high-compression duty of a primary jaw chamber

Machine Data – СМД-111 (ЩДП-9х12)

For fitment confirmation, the host machine data published by the original manufacturer:

• Designation: СМД-111 / ЩДП-9х12
• Feed opening (width × length): 900 × 1200 mm
• Maximum feed lump size: 750 mm
• Overall dimensions (L × W × H): 4,942 × 3,150 × 3,300 mm (excluding drive)
• Machine mass (less components): 54.3 t
• Application: primary crushing of granite, basalt, quartzite, sandstone, limestone and ores
  with a compressive strength up to 300 MPa

Applications

СМД-111 jaw plates are used for primary crushing in hard-rock mining, quarry and aggregate production,
and construction-recycling duties – typically granite, gabbro, basalt and diabase duty in Russian and
CIS crushing plants.

Frequently Asked Questions

Q1. What material grade are the plates supplied in?
Mn18% high-manganese steel as standard. Mn18Cr2 and Mn13Cr2 are available on request for highly abrasive
or high-impact duties.

Q2. Can I buy a single plate rather than the full set?
Yes. Each of the three plates can be ordered separately – just quote the drawing number(s) from the table
above when enquiring.

Q3. What is the lead time?
Machined plates from stock: 7–10 working days. Fresh castings: 25–35 days. Breakdown orders can be
expedited and shipped by airfreight.

Q4. What documentation is supplied?
Every shipment includes spectrometer chemical-composition report, hardness test report and dimensional
inspection report. Third-party inspection (SGS, BV, TÜV) can be arranged on request.

Q5. Is this an OEM part?
No. These are aftermarket replacement parts manufactured by MiningSpares to the original drawings. They are
not affiliated with, or endorsed by, the original equipment manufacturer.

Request a Quotation

For pricing, lead time and alternative material grades on СМД-111 (SMD111) jaw plates, use the
Ajouter à la demande button on this page or email us at
[email protected]. Our sales team responds within one business day.

The post 3440.02.010 / 3440.02.020 / 3440.01.110 Jaw Plates for Russian SMD111 Crusher appeared first on Mining Spares | Crusher Spare Parts ,Drifter Parts ,Slurry Pump Parts.

Items: Concave, Mantle, Concave Ring, Concave Segment, Bowl Liner, Cone Liner, Arm Guard, Distribution Plate
Casting Material: Austenitic Manganese Steel (Mn14, Mn14Cr2, Mn18Cr2, Mn22Cr2)
Méthode de moulage : Coulée de sable au verre d'eau
Applicable Material: Gravel, Granite, Basalt, Ore, Limestone, Sandstone, Quartz, Cobblestone
Applications: Mining, Quarry, Construction, Cement and Materials, Recycling

MiningSpares’ Cedarapids RC54 Bowl Liner and Mantle uses high-quality manganese alloys, including 13% Standard, 18% Premium, and 22% High alloys, to cater to diverse operational requirements and can be customized according to your needs
Nous proposons également différentes couleurs au choix : rouge, bleu, vert, noir, gris, etc.

Rollercone RC54 Mantle & Bowl Liner Specifications

The manufacturing process is very rigorous to ensure a perfect fit with the Cedarapids RC54 Cone Crusher.

Our Rollercone RC54 Mantle & Bowl Liner wear parts are manufactured using advanced casting processes. During the manufacturing process, we strictly control material selection and process flow to ensure excellence in product quality and performance. We use high-quality alloy steel materials, combined with advanced casting technology, to ensure that the wear parts have excellent wear resistance and impact resistance. In addition, our production process includes precision machining and heat treatment processes to further improve the strength and durability of the liners.

For most of the world famous brands like Metso, Sandvik, Terex, Shanbao, Telsmith and so on
Nous disposons tous d'un stock important de dessins originaux, ce qui nous permet de produire à un coût relativement faible.

Related Cone Crusher Wear Parts

Browse more high manganese cone crusher wear parts from MiningSpares:

• PYB1200 Bowl Liner and Mantle
• MX4 Bowl Liner C for Cone Crusher
• H8800 Hydrocone Liner
• Cone Crusher Wear Parts BG00523226

The post EL-Jay Rollercone RC54 Cone Crusher Wear Parts – Mantle & Bowl Liner appeared first on Mining Spares | Crusher Spare Parts ,Drifter Parts ,Slurry Pump Parts.

Product Overview

This is a complete TIC composite wear parts set for the TRIO TP450 Cone Crusher, comprising one Bowl Liner (TRIO17023516) and one Mantle (TRIO17023515). Manufactured from high-manganese steel (Mn18Cr2) with embedded Titanium Carbide (TiC) ceramic composite inserts, these liners deliver 2–3 times the wear life of standard manganese steel parts. Direct-fit replacement — no modifications required.

TIC composite mantle (TRIO17023515) — green cone with visible TiC ceramic inserts (circular dots)

What is TIC Composite Wear Material?

TIC (Titanium Carbide) composite technology represents a major advancement in crusher wear part design. Hard TiC ceramic particles are embedded into a Mn18Cr2 high-manganese steel matrix during the casting process. The result is a wear surface that combines the extreme hardness of ceramics (HV 2400+) with the toughness and impact resistance of manganese steel.

Bowl Liner & Mantle: Working Principle

In a cone crusher, the Manteau (inner moving cone) and the Revêtement de cuvette (outer fixed concave) form the crushing chamber. As the mantle gyrates, rock is compressed and crushed between these two wear surfaces. Both parts are consumable — they wear progressively and must be replaced to maintain crushing efficiency and product gradation.

Bowl liner family — multiple sizes showing TIC composite construction

Key Features & Advantages

• Extended service life: TIC composite delivers 2–3× the wear life of standard Mn18Cr2, reducing downtime and replacement frequency
• Consistent product gradation: Wear-resistant TiC inserts maintain chamber profile longer, ensuring consistent output size throughout the liner lifecycle
• Reduced total cost of ownership: Fewer replacements = less labor, less downtime, lower per-ton crushing cost
• Direct OEM-equivalent fit: Precision-cast to TP450 specifications — drop-in replacement, no modifications needed
• Superior impact resistance: Mn18Cr2 steel matrix absorbs shock loads, preventing brittle fracture of ceramic inserts
• Work-hardening capability: The manganese steel matrix work-hardens under impact, becoming harder with use while TiC inserts provide continuous abrasion resistance
• Universal compatibility: Set includes both mantle and bowl liner for a complete chamber refresh

Typical Applications

Quarrying
Granite, basalt, limestone

Mining
Iron ore, copper, gold ore

Aggregates
Sand & gravel production

Construction
Road base, concrete aggregate

Recycling
Concrete & asphalt recycling

Demolition
Secondary/tertiary crushing

Material & Manufacturing Process

Base material: ASTM A128 Grade Mn18Cr2 — high-manganese austenitic steel with 18% Mn and 2% Cr, providing excellent work-hardening properties and impact toughness.

TIC inserts: Titanium Carbide (TiC) ceramic composite buttons are pre-placed in the mold at high-wear zones before pouring. During casting, the molten steel flows around and bonds with the TiC particles, creating a metallurgical bond between ceramic and steel.

Manufacturing route: Full-mold (lost-foam) casting or precision sand casting → controlled solidification → heat treatment (solution annealing + water quench) → rough and finish machining to OEM dimensions → final inspection.

Quality Control & Inspection

• Chemical composition analysis — Spectrometer verification of Mn, Cr, C, Si, P, S content per ASTM A128
• Mechanical hardness testing — Brinell HB measurement at multiple points (target: HB 220–260 for steel matrix)
• Dimensional inspection — CMM / template gauging against OEM drawings for profile accuracy
• Ultrasonic testing (UT) — Internal defect detection per ASTM E114
• TIC insert verification — Visual and dimensional check of ceramic insert distribution and bond quality
• Surface finish inspection — Visual + dye penetrant testing for surface cracks or defects
• Weight verification — Final weight recorded and compared to nominal (ref. 1312 kg/set)

Packaging & Shipping

Each liner is individually packaged in heat-treated (ISPM-15 compliant) wooden crates with steel banding and anti-corrosion VCI film wrapping. Crates are designed to withstand international container shipping. Suitable for both LCL and FCL container loading. Shipping marks and product labels applied per customer requirements.

Specification Table

The post TRIO17023516 & TRIO17023515 TIC Composite Bowl Liner + Mantle Set for TP450 Cone Crusher appeared first on Mining Spares | Crusher Spare Parts ,Drifter Parts ,Slurry Pump Parts.

Articles : Concave, manteau, anneau concave, segment concave, revêtement de cuvette, revêtement de cône, protection de bras, plaque de distribution.
Matériau de coulée : Acier austénitique au manganèse (Mn14, M14Cr2, Mn18Cr2, Mn22Cr2)
Méthode de moulage : Coulée de sable au verre d'eau
Matériau applicable : gravier, granit, basalte, minerai, calcaire, grès, quatz, pierre de pavé
Applications : Mines, carrières, construction, ciment et matériaux, recyclage

MiningSpares’ HP200 Bowl Liner and Mantle uses high-quality manganese alloys, including 13% Standard, 18% Premium, and 22% High alloys, to cater to diverse operational requirements and can be customized according to your needs
Nous proposons également différentes couleurs au choix : rouge, bleu, vert, noir, gris, etc.

Le processus de fabrication est très rigoureux afin d'assurer une adaptation parfaite au concasseur à cône Cedarapid RC54.

MiningSpares’HP200 Bowl Liner and Mantle are manufactured using advanced casting processes. During the manufacturing process, we strictly control material selection and process flow to ensure excellence in product quality and performance. We use high-quality alloy steel materials, combined with advanced casting technology, to ensure that the blow hammer has excellent wear resistance and impact resistance. In addition, our production process includes precision machining and heat treatment processes to further improve the strength and durability of the blow bars.

Pour la plupart des marques mondialement connues telles que Mettso, Sandvick, Terex, Shanbao, Telsmith, etc.
Nous disposons tous d'un stock important de dessins originaux, ce qui nous permet de produire à un coût relativement faible.

The post HP200 Mantle For Cone Crusher 7055308005 appeared first on Mining Spares | Crusher Spare Parts ,Drifter Parts ,Slurry Pump Parts.

Articles : Concave, manteau, anneau concave, segment concave, revêtement de cuvette, revêtement de cône, protection de bras, plaque de distribution.
Matériau de coulée : Acier austénitique au manganèse (Mn14, M14Cr2, Mn18Cr2, Mn22Cr2)
Méthode de moulage : Coulée de sable au verre d'eau
Matériau applicable : gravier, granit, basalte, minerai, calcaire, grès, quatz, pierre de pavé
Applications : Mines, carrières, construction, ciment et matériaux, recyclage

Le manteau et la chemise de cuve Cedarapid RC54 de MiningSpares utilisent des alliages de manganèse de haute qualité, notamment les alliages 13% Standard, 18% Premium et 22% High, pour répondre à diverses exigences opérationnelles et peuvent être personnalisés en fonction de vos besoins.
Nous proposons également différentes couleurs au choix : rouge, bleu, vert, noir, gris, etc.

Le processus de fabrication est très rigoureux afin d'assurer une adaptation parfaite au concasseur à cône Cedarapid RC54.

Le revêtement de cuve et le manteau Cedarapid RC54 de MiningSpares sont fabriqués à l'aide de procédés de moulage avancés. Au cours du processus de fabrication, nous contrôlons strictement la sélection des matériaux et le déroulement du processus afin de garantir l'excellence de la qualité et des performances du produit. Nous utilisons des matériaux en acier allié de haute qualité, combinés à une technologie de moulage avancée, pour garantir que le marteau souffleur présente une excellente résistance à l'usure et aux chocs. En outre, notre processus de production comprend des procédés d'usinage de précision et de traitement thermique afin d'améliorer encore la résistance et la durabilité des barres de soufflage.

Pour la plupart des marques mondialement connues telles que Mettso, Sandvick, Terex, Shanbao, Telsmith, etc.
Nous disposons tous d'un stock important de dessins originaux, ce qui nous permet de produire à un coût relativement faible.

The post Bowl Liner and Mantle Suit EL-Jay Rollercone RC54 Cone crusher appeared first on Mining Spares | Crusher Spare Parts ,Drifter Parts ,Slurry Pump Parts.

Le Spider Cap KB63-89 de Wearplus utilise des alliages de manganèse de haute qualité, notamment les alliages 13% Standard, 18% Premium et 22% High, pour répondre aux diverses exigences opérationnelles et peut être personnalisé en fonction de vos besoins.
Nous proposons également différentes couleurs au choix : rouge, bleu, vert, noir, gris, etc.

Le processus de fabrication est très strict afin de garantir une adaptation parfaite à la machine.

Les capuchons d'araignée KB63-89 de MiningSpares sont fabriqués à l'aide de procédés de moulage avancés. Au cours du processus de fabrication, nous contrôlons strictement la sélection des matériaux et le déroulement du processus afin de garantir l'excellence de la qualité et des performances du produit. Nous utilisons des matériaux en acier allié de haute qualité, combinés à une technologie de moulage avancée, pour garantir que le marteau-pilon présente une excellente résistance à l'usure et aux chocs. En outre, notre processus de production comprend des procédés d'usinage de précision et de traitement thermique afin d'améliorer encore la résistance et la durabilité des barres de soufflage.

Pour la plupart des marques mondialement connues telles que Mettso, Sandvick, Terex, Shanbao, Telsmith, etc.
Nous disposons tous d'un stock important de dessins originaux, ce qui nous permet de produire à un coût relativement faible.

The post KB63-89 Spider Cap For Gyratory Crusher 4350760 appeared first on Mining Spares | Crusher Spare Parts ,Drifter Parts ,Slurry Pump Parts.

Le manteau GP7 de Wearplus utilise des alliages de manganèse de haute qualité, notamment les alliages 13% Standard, 18% Premium et 22% High, pour répondre aux diverses exigences opérationnelles et peut être personnalisé en fonction de vos besoins.
Nous proposons également différentes couleurs au choix : rouge, bleu, vert, noir, gris, etc.

Le processus de fabrication est très strict afin de garantir une adaptation parfaite à la machine.

Les manchons GP7 de Wearplus sont fabriqués à l'aide de procédés de moulage avancés. Au cours du processus de fabrication, nous contrôlons strictement la sélection des matériaux et le déroulement du processus afin de garantir l'excellence de la qualité et des performances du produit. Nous utilisons des matériaux en acier allié de haute qualité, combinés à une technologie de moulage avancée, pour garantir que le marteau souffleur présente une excellente résistance à l'usure et aux chocs. En outre, notre processus de production comprend des procédés d'usinage de précision et de traitement thermique afin d'améliorer encore la résistance et la durabilité des barres de soufflage.

Pour la plupart des marques mondialement connues telles que Mettso, Sandvick, Terex, Shanbao, Telsmith, etc.
Nous disposons tous d'un stock important de dessins originaux, ce qui nous permet de produire à un coût relativement faible.

The post GP7 Mantle For Cone Crusher MM1120649 appeared first on Mining Spares | Crusher Spare Parts ,Drifter Parts ,Slurry Pump Parts.

Le contre-batteur GP7 de MiningSpares utilise des alliages de manganèse de haute qualité, notamment les alliages 13% Standard, 18% Premium et 22% High, pour répondre aux diverses exigences opérationnelles et peut être personnalisé en fonction de vos besoins.
Nous proposons également différentes couleurs au choix : rouge, bleu, vert, noir, gris, etc.

Le processus de fabrication est très strict afin de garantir une adaptation parfaite à la machine.

La partie supérieure du contre-batteur GP7 de MiningSpares est fabriquée à l'aide de procédés de moulage avancés. Au cours du processus de fabrication, nous contrôlons strictement la sélection des matériaux et le déroulement du processus afin de garantir l'excellence de la qualité et des performances du produit. Nous utilisons des matériaux en acier allié de haute qualité, combinés à une technologie de moulage avancée, pour garantir que le marteau-pilon présente une excellente résistance à l'usure et aux chocs. En outre, notre processus de production comprend des procédés d'usinage de précision et de traitement thermique afin d'améliorer encore la résistance et la durabilité des barres de soufflage.

Pour la plupart des marques mondialement connues telles que Mettso, Sandvick, Terex, Shanbao, Telsmith, etc.
Nous disposons tous d'un stock important de dessins originaux, ce qui nous permet de produire à un coût relativement faible.

The post GP7 Concave upper For Cone Crusher MM1107643 appeared first on Mining Spares | Crusher Spare Parts ,Drifter Parts ,Slurry Pump Parts.

Le contre-batteur GP7 de MiningSpares utilise des alliages de manganèse de haute qualité, notamment les alliages 13% Standard, 18% Premium et 22% High, pour répondre aux diverses exigences opérationnelles et peut être personnalisé en fonction de vos besoins.
Nous proposons également différentes couleurs au choix : rouge, bleu, vert, noir, gris, etc.

Le processus de fabrication est très strict afin de garantir une adaptation parfaite à la machine.

Le contre-batteur GP7 de MiningSpares est fabriqué à l'aide de procédés de moulage avancés. Au cours du processus de fabrication, nous contrôlons strictement la sélection des matériaux et le déroulement du processus afin de garantir l'excellence de la qualité et des performances du produit. Nous utilisons des matériaux en acier allié de haute qualité, combinés à une technologie de moulage avancée, pour garantir que le marteau-pilon présente une excellente résistance à l'usure et aux chocs. En outre, notre processus de production comprend des procédés d'usinage de précision et de traitement thermique afin d'améliorer encore la résistance et la durabilité des barres de soufflage.

Pour la plupart des marques mondialement connues telles que Mettso, Sandvick, Terex, Shanbao, Telsmith, etc.
Nous disposons tous d'un stock important de dessins originaux, ce qui nous permet de produire à un coût relativement faible.

The post GP7 Concave Lower For Cone Crusher MM1107642 appeared first on Mining Spares | Crusher Spare Parts ,Drifter Parts ,Slurry Pump Parts.